Continuous-reactor, pH-controlled synthesis of multifunctional mesoporous nanocrystalline anatase aggregates

X-Ray Diffractometer (XRD) application in the research of the phase identification, crystal lattice structure and calculate crystal size
MIAM | 1 Apr 2016

Continuous-reactor, pH-controlled synthesis of multifunctional mesoporous nanocrystalline anatase aggregates

Research Published at:听, , , 1 March 2016, Pages 398-409

Authors:听Benedetto Marelli,鈥� Chiara E. Ghezzi,鈥� Jake E. Barralet,鈥� Aldo R. Boccaccini,搂 and Showan N. Nazhat*,鈥�

  • Department of Mining and Materials Engineering, Faculty of Dentistry, 成人VR视频,
  • Department of Materials Science and Engineering, University of Erlangen-Nuremberg, Germany

Research Method:

For phase identification, X-ray diffraction (XRD) was performed. scanning took place between 20掳 and 70掳 (2h) with 0.005掳step/second. Background subtraction and smoothening were performed on EVA software. The XRD patterns were compared against JCPDS reference data of anatase (#00-021-1272). Crystallite size was determined using following Scherrer equation:

Dhkl = k位/(尾 cos胃)

Where, Dhkl is crystal size in nm, k is 0.89, k is wavelength of Cu radiation (0.1549 nm), b is FWHM (Full Width at Half Maximum) corresponding to (hkl) plane in radians, and h is the Bragg angle corresponding to (hkl) plane in radians.

XRD research fig听

Fig. 3.听XRD patterns of TiO2听products synthesized at: (a) 70听掳C, (b) 80听掳C, and (c) 90听掳C compared to听anatase听reference pattern. Constant conditions: [TiCl4]feed听=听0.1听M, pHsteady-state听=听3,听蟿: 30听min.

Rutile peak at 27.5掳 is evident. At pH 6 the product became amorphous.

XRD research fig 2

Fig. 4.听XRD patterns of steady state products compared to听anatase听reference pattern: The effect of pH: (a) pH 2, (b) pH 3, (c) pH 4, (d) pH 5; constant conditions:听T听=听80听掳C, [TiCl4]feed听=听0.1听M,听蟿听=听30听min. The effect of [TiCl4]feed: (e) 0.1听M, (f) 0.2听M, (g) 0.3听M, (h) 0.4听M, (i) 0.5听M; constant conditions:听T听=听80听掳C, pHsteady-state听=听3,听蟿听=听30听min.

Results:

  • XRD patterns show all characteristic of body-centered tetragonal anatase phase, according to JCPDS #00-021-1272 (data base);
  • The peaks are broad and low density, indicative of nano-sized-crystals;
  • The average diameters of the anatase crystallites (4.01~ 5.5 nm) nicely agree with the TEM crystallite size data;
  • The peaks overall get shorter and broader, revealing a decrease in crystallinity.